I have one plate SA 516 Gr. 70N + SS 316L Clad (Explosion Bonding) to form as a head. After formed, percent of elongation is more than 5% and as per UCS-79, stress relief is required, but our client request to do normalizing method with temperature 900⁰C to 960⁰C. So, with this temperature, Clad can be stand or not. could anyone advice me regarding this matter.

Kindly, prompt respond are appreciated.

Thank you.

_________________
Faizol
(PV-elite User)

Hi Faizol

Why don't you ask cleint to go for SR , As normalizing may impart the corrosion reistant property for SS CS combination.
What is the thickness can you tell us?then we can find out some way out of code.

_________________
Niraj

I dont have any adive on this but i cant help and notice this job sounds just like a scam that a man was pulling on USA companies for a long time. He would promise endless head work overlays and the like.
not saying this is the case but all in this industry sould watch out because he is still out there i have the names he uses if any1 wants em
MDK